Method for making charged nanoparticles

ABSTRACT

The disclosure relates to a method for making charged nanoparticles, the method includes: providing a solution with a first solute; atomizing the solution into micro-scaled droplets; providing a charged electrode with at least one through-hole, a negative or positive electric potential is applied to the electrode; allowing the micro-scaled droplets to pass through the at least one through-hole.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a continuation application of U.S. patent application Ser. No. 15/598218, filed on May 17, 2017, entitled, “DEVICE FOR MAKING CHARGED NANOPARTICLES”, which claims all benefits accruing under 35 U.S.C. § 119 from China Patent Application No. 201610336947.9, tiled on May 20, 2016, in the China National Intellectual Property Administration, the contents of which are hereby incorporated by reference. The disclosures of the above-identified applications are incorporated herein by reference.

BACKGROUND 1. Technical Field

The subject matter herein generally relates to a device for making charged nanoparticles.

2. Description of Related Art

Nanoparticles are a kind of micro-particles with a diameter of nanometer. At present there are many methods and devices for making nanoparticles. Different methods and devices can lead to different performance and particle size. However, there has not been a method and device which can directly obtain charged nanoparticles.

What is needed, therefore, is to provide a method and device for making charged nanoparticles which can overcome the shortcomings as described above.

BRIEF DESCRIPTION OF THE DRAWINGS

Many aspects of the embodiments can be better understood with reference to the following drawings. The components in the drawings are not necessarily drawn to scale, the emphasis instead being placed upon clearly illustrating the principles of the embodiments. Moreover, in the drawings, like reference numerals designate corresponding parts throughout the several views.

FIG. 1 is a schematic view of one embodiment of a method for detecting surface electric field distribution of nanostructures.

FIG. 2 is an exploded view of one embodiment of a vapor-condensation-assisted device.

FIG. 3 is a schematic view of one embodiment of a vapor-condensation-assisted device.

FIG. 4 is a schematic view of one embodiment of an optical microscope and a vapor-condensation-assisted device.

FIG. 5 is an optical image of ultra-long carbon nanotubes taken by the method for detecting surface electric field distribution of nanostructures of FIG. 1.

FIG. 6 is a scanning electron microscope (SEM) image of the ultra-long carbon nanotubes in FIG. 5.

FIG. 7 is a schematic view of one embodiment of a device to study the relationship between the dark strips' width and the nanostructure sample's voltage.

FIG. 8 is an optical image of ultra-long carbon nanotubes in accordance with FIG. 7.

FIG. 9 is a schematic view of the relationship between the dark strips' width and nanostructure sample's voltage.

FIG. 10 is a schematic view of the relationship between the dark strips' width and the silicon dioxide layer's thickness.

FIG. 11 is a schematic view of one embodiment of a device for making charged nanoparticles.

DETAILED DESCRIPTION

It will be appreciated that for simplicity and clarity of illustration, where appropriate, reference numerals have been repeated among the different figures to indicate corresponding or analogous elements. In addition, numerous specific details are set forth in order to provide a thorough understanding of the embodiments described herein. However, it will be understood by those of ordinary skill in the art that the embodiments described herein can be practiced without these specific details. In other instances, methods, procedures, and components have not been described in detail so as not to obscure the related relevant feature being described. The drawings are not necessarily to scale, and the proportions of certain parts may be exaggerated to be better illustrate details and features. The description is not to considered as limiting the scope of the embodiments described herein.

Several definitions that apply throughout this disclosure will now be presented.

The connection can be such that the objects are permanently connected or releasably connected. The term “outside” refers to a region that is beyond the outermost confines of a physical object. The term “inside” indicates that at least a portion of a region is partially contained within a boundary formed by the object. The term “substantially” is defined to essentially conforming to the particular dimension, shape or other word that substantially modifies, such that the component need not be exact. For example, substantially cylindrical means that the object resembles a cylinder, but can have one or more deviations from a true cylinder. The term “comprising” means “including, but not necessarily limited to”; it specifically indicates open-ended inclusion or membership in a so-described combination, group, series and the like. It should be noted that references to “an” or “one” embodiment in this disclosure are not necessarily to the same embodiment, and such references mean at least one.

References will now be made to the drawings to describe, in detail, various embodiments of the present epitaxial structures and methods for making the same.

Referring to FIG. 1, a method for detecting surface electric field distribution of nanostructures of one embodiment is provided. The method comprises the steps of:

-   -   step (S11), providing a nanostructure sample 60 located on an         insulated layer 614 of a substrate 610;     -   step (S12), spraying first charged nanoparticles 620 to the         insulated layer 614; and     -   step (S13), blowing vapor to the insulated layer 614 to observe         the distribution of the first charged nanoparticles 620 via an         optical microscope.

In step (S11), the nanostructure sample 60 can be any pattern with a nanostructure. For example, the nanostructure sample 60 can be zero-dimensional nanomaterials, one-dimensional nanomaterials, or two-dimensional nanomaterials.

In one embodiment, the nanostructure sample 60 comprises ultra-long carbon nanotubes horizontally aligned on the substrate 614. The diameter of the ultra-long carbon nanotubes can range from about 0.5 nanometers to about 10 nanometers. The length of the ultra-long carbon nanotubes is equal to or huger than 50 micrometers.

The substrate 610 has an insulated layer 614 so that charges cannot transfer from the nanostructure sample 60 to the substrate 610.

In one embodiment, the substrate 610 can be a silicon substrate with a silicon dioxide layers located on the surface of the silicon substrate. The thickness of the silicon dioxide layers is about 0.1 micrometers to about 1 micrometer.

In step (S12), the pre-charged nanoparticles 620 are sprayed to the insulated layer 614 uniformly. The diameter of the pre-charged nanoparticles 620 can range from about 0.5 nanometers to about 5 nanometers. The first charged nanoparticles 620 are all positively charged or all negatively charged. The first charged nanoparticle 620 can be crystals difficult to sublimate, for example, charge( glucose nanoparticles, charged sucrose nanoparticles, charged metal salt nanoparticles, or the like. The anions of the charged metal salt nanoparticles can be chloride, nitrate, sulfate, and the metal cations can be Na, K, Ca, Fe. In one embodiment, the first charged nanoparticles 620 are charged NaCl nanoparticles.

In step (S13), the vapor can be water vapor or ethanol vapor. When the vapor reaches the insulated layer 614, the vapor would condense into micro-droplets which are attached to the nanostructure sample 60 and the first charged nanoparticle 620. Under oblique illumination light, the micro-droplets will act as scattering, centers, appearing as bright dots under a dark-field optical microscope. Thus, the nanostructure sample 60 and the first charged nanoparticle 620 are observed by the optical microscope.

Like charges repel each other, but opposite charges attract due to Coulomb interaction. If the first charged nanoparticles 620 and the nanostructure sample 60 have the same sign, the electrostatic force between them is repulsive, the first charged nanoparticles 620 will avoid the nanostructure sample 60. If the first charged nanoparticles 620 and the nanostructure sample 60 have different signs, the force between them is attractive, the first charged nanoparticles 620 will aggregate at the nanostructure sample 60. Thus an image of surface charge distribution will be delineated by the first charged nanoparticles 620.

Referring to FIG. 5 and FIG. 6, the first charged nanoparticles 620 avoid the nanostructure sample 60, so the first charged nanoparticles 620 and the nanostructure sample 60 have the same sign.

The method of providing the vapor is not limited. In one embodiment, the vapor is produced via a vapor-condensation-assisted device 20. Referring to FIG. 2, the vapor-condensation-assisted device 20 comprises an air blowing device 210, a vapor producing device 220 and a guide pipe 230. The air blowing device 210 is connected to the vapor producing device 220 and can blow air into the vapor producing device 220. The vapor producing device 220 is connected to the guide pipe 230. The air can blow from the air blowing device 210 into the vapor producing device 220 and out of the guide pipe 230. The vapor produced in the vapor producing device 220 can be blown to the surface 614 by the blowing air from the air blowing device 210.

The air blowing device 210 can be a flexible bulb that is able to inhale or exhale the air by pressing. The air bowling device 210 is connected to the vapor producing device 220. The air can be blown into the vapor producing device 220 by the air blowing device 210. In one embodiment, the air blowing device 210 is a rubber suction bulb.

The vapor producing device 220 comprises a liquid absorbing material 222, a hollow tube 224, a heating layer 226 and a power source 228. The liquid absorbing material 222 is located in the hollow tube 224, but does not affect the ventilation performance of the hollow tube 224. A liquid material is absorbed by the liquid absorbing material 222. The heating layer 226 is surrounded the out surface of the hollow tube 224 and electrical connected to the power source 228. The heating layer 226 is used to heat the liquid absorbing material 222 located in the hollow tube 224.

A material of the hollow tube 224 is not limited, and can be soft or hard materials. The hard material can be ceramic, glass, or quartz. The soft material can be resin, rubber, plastic or flexible fiber. The cross-section shape of the hollow tube 224 is not limited, and can be round, arc, or rectangle.

In one embodiment, the hollow tube 224 is a hollow ceramic tube with a circular cross section. The diameter of the hollow ceramic tube is about 1 centimeter, and the length of the hollow ceramic tube is about 6 centimeters.

The liquid absorbing material 222 has good absorption performance. The liquid absorbing material 222 can be cotton, non-woven fabrics and high absorbent resin. In one embodiment, the liquid absorbing material 222 is attached to the inner surface of the hollow tube 224.

The heating layer 226 is disposed on an outer surface of the hollow tube 224. The heating layer 226 comprises a carbon nanotube structure. The carbon nanotube structure includes a plurality of carbon nanotubes uniformly distributed therein, and the carbon nanotubes therein can be combined by van der Waals attractive force therebetween. The carbon nanotube structure can be a substantially pure structure of the carbon nanotubes, with few impurities. The carbon nanotubes can be used to form many different structures and provide a large specific surface area. The heat capacity per unit area of the carbon nanotube structure can be less than 2×10−4 J/m²·K. Typically, the heat capacity per unit area of the carbon nanotube structure is less than 1.7×10−6 J/m²·K. As the heat capacity of the carbon nanotube structure is very low, and the temperature of the heating element 16 can rise and fall quickly, which makes the heating layer 226 have a high heating efficiency and accuracy. As the carbon nanotube structure can be substantially pure, the carbon nanotubes are not easily oxidized and the life of the heating layer 226 will be relatively long. Further, the carbon nanotubes have a low density, about 1.35 g/cm³, so the heating layer 226 is light. As the heat capacity of the carbon nanotube structure is very low, the heating layer 226 has a high response heating speed. As the carbon nanotube has large specific surface area, the carbon nanotube structure with a plurality of carbon nanotubes has large specific surface area. When the specific surface of the carbon nanotube structure is large enough, the carbon nanotube structure is adhesive and can be directly applied to the outer surface of the hollow tube 224.

The carbon nanotubes in the carbon nanotube structure can be arranged orderly or disorderly. The term ‘disordered carbon nanotube structure’ refers to a structure where the carbon nanotubes are arranged along many different directions, and the aligning directions of the carbon nanotubes are random. The number of the carbon nanotubes arranged along each different direction can be almost the same (e.g. uniformly disordered). The disordered carbon nanotube structure can be isotropic. The carbon nanotubes in the disordered carbon nanotube structure can be entangled with each other.

The carbon nanotube structure including ordered carbon nanotubes is an ordered carbon nanotube structure. The term ‘ordered carbon nanotube structure’ refers to a structure where the carbon nanotubes are arranged in a consistently systematic manner, e.g., the carbon nanotubes are arranged approximately along a same direction and/or have two or more sections within each of which the carbon nanotubes are arranged approximately along a same direction (different sections can have different directions). The carbon nanotubes in the carbon nanotube structure can be selected from a group consisting of single-walled, double-walled, and/or multi-walled carbon nanotubes.

The carbon nanotube structure can be a carbon nanotube film structure with a thickness ranging from about 0.5 nanometers to about 1 millimeter. The carbon nanotube film structure can include at least one carbon nanotube film. The carbon nanotube structure can also be a linear carbon nanotube structure with a diameter ranging from about 0.5 nanometers to about 1 millimeter. The carbon nanotube structure can also be a combination of the carbon nanotube film structure and the linear carbon nanotube structure. It is understood that any carbon nanotube structure described can be used with all embodiments. It is also understood that any carbon nanotube structure may or may not employ the use of a support structure.

In one embodiment, the carbon nanotube structure includes at least one drawn carbon nanotube film. A film can be drawn from a carbon nanotube array, to form a drawn carbon nanotube film. The drawn carbon nanotube film includes a plurality of successive and oriented carbon nanotubes joined end-to-end by van der Waals attractive force therebetween. The drawn carbon nanotube film is a free-standing film. Each drawn carbon nanotube film includes a plurality of successively oriented carbon nanotube segments joined end-to-end by van der Waals attractive force therebetween. Each carbon nanotube segment includes a plurality of carbon nanotubes parallel to each other, and combined by van der Waals attractive force therebetween. As can be seen in FIG. 3, some variations can occur in the drawn carbon nanotube film. The carbon nanotubes 145 in the drawn carbon nanotube film are oriented along a preferred orientation. The carbon nanotube film can be treated with an organic solvent to increase the mechanical strength and toughness of the carbon nanotube film and reduce the coefficient of friction of the carbon nanotube film. A thickness of the carbon nanotube film can range from about 0.5 nanometers to about 100 micrometers.

The vapor producing device 220 further comprises two electrodes 221 located on and electrically connected to the heating layer 226. Furthermore, it is imperative that the two spaced electrodes 221 are separated from each other to prevent short circuiting of the electrodes. The two electrodes 221 can be directly electrically attached to the heating layer 226 by, for example, a conductive adhesive (not shown), such as silver adhesive. Because, some of the carbon nanotube structures have large specific surface area and are adhesive in nature, in some embodiments, the two electrodes 221 can be adhered directly to heating layer 226. It should be noted that any other bonding ways may be adopted as long as the two electrodes 221 are electrically connected to the heating layer 226. The shape of the two electrodes 221 are not limited and can be lamellar, rod, wire, and block among other shapes.

The two electrodes 221 can be conductive films. A material of the two electrodes 221 can be metal, alloy, indium tin oxide (ITO), antimony tin oxide (ATO), conductive silver glue, conductive polymers or conductive carbon nanotubes. The metal or alloy materials can be aluminum, copper, tungsten, molybdenum, gold, titanium, neodymium, palladium, cesium or any combination of the alloy. In one embodiment, the electrode 221 is a palladium film with a thickness of 20 nanometers.

The power source 228 can be AC or DC power. The power source 228 is electrically connected to the two electrodes 221. When a voltage is applied to heating layer 226 via the two electrodes 221, the carbon nanotube structure of the heating layer 226 radiates heat at a certain wavelength. The temperature of the heating layer 226 ranges from 30° C. to 300° C., the liquid material in the liquid absorbing material 222 turns to vapor.

The vapor producing device 220 can further comprises a protecting layer 202 attached to the exposed surface of the heating layer 226. The protecting layer 202 can protect the heating layer 226 from the environment. A material of the protecting layer 202 can be an insulated material, such as resin, plastic or rubber. A thickness of the protecting layer 202 can range from about 0.5 μm to about 2 mm.

The guide pipe 230 comprises a first opening 231 and a second opening 235 opposite to the first opening 231. The diameter of the first opening 231 is smaller than the diameter of the second opening 235. Air can flow from the first opening 231 to the second opening through the guide pipe 230. The second opening 235 is sealed connected to the vapor producing device 220. The material of the guide pipe 230 is not limited, and can be soft or hard materials. The hard material can be ceramic, glass, or quartz. The soft material can be resin, rubber, plastic or flexible fiber. The cross section shape of the hollow tube 224 is also unlimited, and can be round, arc, or rectangle. In one embodiment, this example, the guide pipe 230 is a hollow ceramic tube with a circular cross section.

The air blowing device 210, the vapor producing device 220 and the guide pipe 230 are integrated with each other. The air blowing device 210 can push the air through the vapor producing device 220 and the guide pipe 230, from the first opening 231 to the nanostructure sample 60 on the stage 110.

Referring to FIG. 3, the vapor-condensation-assisted device 20 can further comprises an additional pipe 240. The additional pipe 240 is located between the vapor producing device 220 and the air blowing device 210. The vapor producing device 220 is connected to the air blowing device 210 via the additional pipe 240. The material of the additional pipe 240 is not limited, and can be soft or hard materials. The hard material can be ceramic, glass, or quartz. The soft material can be resin, rubber, plastic or flexible fiber. The stability of air flow can be enhanced by the additional pipe 240. In one embodiment, the additional pipe 240 is made of rubber, and 50 centimeters long.

When the vapor-condensation-assisted device 20 is applied, the first opening 231 of the guide pipe 230 can be immersed into liquid and inhale some liquid into the vapor producing device 220. The liquid inhaled in the vapor producing device 220 is absorbed by the liquid absorbing material 222. When the vapor producing device 220 is heated by the heating layer 226, vapor is obtained and can flow with the air flow from the air bowling device 210 to the first opening 231. The vapor is induced to the surface of the nanostructure sample 60. The liquid can be water or alcohol. In one embodiment, the liquid is water, the vapor is water vapor.

The optical microscope 10 can be one of various optical microscopes existing technology. Referring to FIG. 4, in one embodiment, the optical microscope 10 comprises stage 110, objective lenses 120, eyepiece 130, and an image collecting system 140, a light source system 150 and focus adjusting system 160.

The stage 110 is a platform below the objective lenses 120 which supports the specimen being viewed. The objective lenses 120 are usually in a cylinder housing containing a glass single or multi-element compound lens. The optical microscope 10 can comprises one or more objective lenses 120 that collect light from the specimen. In one embodiment, there are around three objective lenses 120 screwed into a circular nose piece which may be rotated to select the required objective lens 120. These arrangements are designed to be par focal, which means that when one changes from one lens to another on a microscope, the specimen stays in focus. The image collecting system 140 comprises a computer 144 and a camera 142. The focus adjusting system 160 comprises focus knobs to move the stage 110 up and down with separate adjustment for coarse and fine focusing. Many sources of light can be used as the light source system 150. At its simplest, daylight can be directed via a mirror.

The substrate 610 can be located on the stage 110. The substrate 610 can be observed by adjusting the focusing mechanism of the optical microscope system 100. The nanostructure sample 60 cannot be observed by the optical microscope system 100, when the vapor is not induced to the surface of the nanostructure sample 60. When the vapor reaches the insulated layer 614, the vapor would condense into micro-droplets which are attached to the nanostructure sample 60 and the first charged nanoparticle 620. Under oblique illumination light, the micro-droplets of water will act as scattering centers, appearing as bright dots under a dark-field optical microscope. Thus, the nanostructure sample 60 and the first charged nanoparticle 620 can be observed by the optical microscope.

A method for calculating surface electric field distribution of nanostructures of one embodiment is also provided. The method comprises the steps of:

-   -   step (S31), providing a nanostructure sample 60 located on an         insulated layer 614 of a substrate 610;     -   step (S32), spraying first charged nanoparticles 620 onto the         insulated layer 614, wherein the first charged nanoparticles 620         and the nanostructure sample 60 are all positively charged or         all negatively charged;     -   step (S33), blowing vapor to the insulated layer 614 and imaging         the first charged nanoparticles 620 via an optical microscope,         and recording the width w between the first charged         nanoparticles 620 and the nanostructure sample 60; and     -   step (S34), obtaining the voltage U of the nanostructure sample         60 by a equation

${w = \left( {\frac{F_{c}}{32\left( {U - U_{0}} \right)D^{2}}{\ln\left( \frac{2{D/d}}{2^{1/\epsilon_{r}}} \right)}} \right)^{{- 1}/3}},$ wherein F_(c) is the constant three from the first charged nanoparticles 620 flow, U₀ is the threshold voltage of the nanostructure sample 60, D is d is the thickness of the insulated layer, d is the diameter of the nanostructure sample 60, ϵ_(r) equals to ϵ/ϵ₀, ϵ is a permittivity of the insulated layer, and ϵ₀ is a permittivity of vacuum.

In step (S32), the first charged nanoparticles 620 and the nanostructure sample 60 have the same sign. For example, if the nanostructure sample 60 is positively charged, then the first charged nanoparticles 620 applied to the insulated layer 614 is also positively charged; if the nanostructure sample 60 is negatively charged, then the first charged nanoparticles 620 applied to the insulated layer 614 is also negatively charged.

In step (S33), owing to the first charged nanoparticles 620 and the nanostructure sample 60 have the same sign, there is a dark strip between the first charged nanoparticles 620 and the nanostructure sample 60 in the optical image under the optical microscope. The width w between the first charged nanoparticles 620 and the nanostructure sample 60 can be obtained by measuring the width of the dark strip.

In step (S34), referring to FIG. 7, the nanostructure sample 60 to be observed is ultra-long semiconducting carbon nanotubes, the insulated layer 614 is silicon dioxide layer. To study the relationship between the width w and the voltage U of the nanostructure sample 60, the ultra-long semiconducting carbon nanotubes are connected with a positively charged electrode 612. The first charged nanoparticles 620 are also positively charged. Referring to FIG. 8, the dark strip between the first charged nanoparticles 620 and the nanostructure sample 60 reflect the positive surface charge distribution along the carbon nanotubes. Referring to FIG. 9, the dark strip become wider with the increase of the voltage applied to the charged electrode 612. Referring to FIG. 10, the dark strip become wider with the increase of the thickness of the silicon dioxide layer.

To clearly understand the mechanism, the following derivation is made.

For a cylinder electric field, the amplitude is given by

$\begin{matrix} {{E_{c} = \frac{\lambda}{2\;\pi\;\epsilon_{0}r}},} & (1) \end{matrix}$

-   -   where λ is the linear charge density of a CNT, ϵ_(D) is the         permittivity of vacuum, r is the radius. Due to the influence of         image charge, the total electric filed between the CNT and the         conducting substrate is given by

$\begin{matrix} {{E = {\frac{\lambda}{2\;\pi\;\epsilon_{0}r} + \frac{\lambda}{2\;\pi\;{\epsilon\left( {{2D} + d - r} \right)}}}},} & (2) \end{matrix}$

-   -   where D is the thickness of the silicon dioxide layer, d is the         diameter of the CNT, ϵ is the permittivity of the silicon         dioxide layer. Here, the influence of polarization charge is         ignored. Actually, it could be reduced in ϵ. Then the capacity         is given by

$\begin{matrix} {{C = {\frac{\lambda}{U} = {{\lambda/{\int_{d/2}^{{d/2} + D}{Edr}}} = {{1/{\int_{d/2}^{{d/2} + D}{\left( {\frac{1}{2\;\pi\;\epsilon_{0}r} + \frac{1}{2\;\pi\;{\epsilon\left( {{2D} + d - r} \right)}}} \right){dr}}}} = \frac{2\;\pi\;\epsilon_{0}}{\ln\left( \frac{2{D/d}}{2^{1}/\epsilon_{r}} \right)}}}}},} & (3) \end{matrix}$

-   -   where ϵ_(r) equals to ϵ/ϵ_(D), and D»d is used. Considering the         flow is nearly constant, the boundary of dark strip is the         equilibrium position of electric force and the pressure         difference, the following relationship is obtained

$\begin{matrix} {{{{C\left( {U - U_{D}} \right)}\left( {\frac{1}{\pi\;\epsilon_{0}w} - \frac{w/2}{2\;\pi\;{\epsilon_{0}\left( {{4D^{2}} + {w^{2}/4}} \right)}}} \right)} = F_{c}},} & (4) \end{matrix}$

-   -   where U is the gate voltage, U_(D) is the threshold voltage of         semiconducting carbon nanotubes, w is the width of dark strips,         F_(c) is the constant force from the flow. After transformation         and simplification of (4), the relationship between w and U is,         where w»D is used.

$\begin{matrix} {{U = {{\frac{\pi\;\epsilon_{0}F_{c}}{16\;{CD}^{2}}w^{3}} + U_{D}}},} & (5) \end{matrix}$

The theoretical curve fits the experimental data well as shown in FIG. 9. Furthermore, The relationship between the width of dark strips and, the thickness of the silicon dioxide layer is

$\begin{matrix} {w = {\left( {\frac{F_{c}}{32\left( {U - U_{D}} \right)D^{2}}{\ln\left( \frac{2{D/d}}{2^{1/\epsilon_{r}}} \right)}} \right)^{{- 1}/3}.}} & (6) \end{matrix}$

With equation (6), FIG. 10 shows the plot and fitted curve of dark strips' width and the thickness of silicon dioxide layer. Due to the quantitative analysis, the value of the surface electric field distribution, sometimes the surface charge distribution can be obtained after calibration for other conditions.

Referring to FIG. 11, a device 700 for making charged nanoparticles 620 of one embodiment is provided. The device 700 includes an atomizer 710, a first electrode 720, and a second electrode 730. The atomizer 710 and the first electrode 720 are spaced apart from each other, and the first electrode 720 is located between the atomizer 710 and the second electrode 730.

The atomizer 710 is configured to atomize a solution into micro-scaled droplets. In one embodiment, the solution is NaCl saturated ethanol solution, the NaCl saturated ethanol solution is converted into micro-scaled ethanol drop with saturated NaCl by the atomizer 710. The atomizer 710 can be a compressed air atomizer.

The first electrode 720 and the second electrode 730 are planar structures substantially parallel with and spaced from each other. There can be at least one first through-hole 722 is defined on the first electrode 720; similarly, there can be at least one second through-hole 732 is defined on the second electrode 730. The micro-scaled droplets atomized by the atomizer 710 can pass through the first electrode 720 and the second electrode 730 via the at least one first through-hole 722 and the at least one second through-hole 732. The charged nanoparticles 620 obtained by device 700 can have a good performance when the diameter of the at least one first through-hole 722 and the at least one second through-hole 732 is equal to or less than 1 millimeter. In one embodiment, both of the first electrode 720 and the second electrode 730 are metal-grid.

A voltage U₁₂ is applied between the first electrode 720 and the second electrode 730. The voltage U₁₂ can range from about −2000V to about +2000V. In one embodiment, the potential of the second electrode 730 is about +1800V or about −1800V. When the micro-scaled droplet atomized by the atomizer 710 is passing through the charged electrode, the electrons can transfer between the charged electrode and the micro-scaled droplets. The sign of the micro-scaled droplets depends on the sign of the charged second electrode 730. For example, the charged second electrode 730 is negative, the electrons transferred from the charged second electrode 730 to the micro-scaled droplets.

A device for making charged nanoparticles 620 of one embodiment is provided. The device includes an atomizer 710 and a metal-grid. The atomizer 710 is configured to atomize a solution into micro-sealed droplets. The metal-grid has a plurality of holes, the metal-grid is applied with a negative or positive electric potential ranged from about −2000V to about +2000V so that electrons are transferred between the metal-grid and the micro-scaled droplets when the micro-sealed droplets passing through the plurality of holes. In one embodiment, the negative or positive electric potential is about −1800V or about +1800V.

A method for making charged nanoparticles of one embodiment is further provided. The method comprises the step of:

-   -   step (S41), providing a solution;     -   step (S42), atomizing the solution into micro-scaled droplets;     -   step (S43), providing a charged electrode with at least one         through-hole, the electrode is applied to a negative or positive         electric potential;     -   step(S44), allowing the micro-scaled droplets to pass through         the at least one through-hole.

In step (S41), the solution can be a saturated solution with a volatile solvent. The solute of the solution is decided by the charged nanoparticles to be prepared. The solvent of the solution can be water or ethanol. For example, to prepare charged NaCl nanoparticles the solution to be atomized can be NaCl saturated ethanol solution; or to prepare charged glucose nanoparticles the solution to be atomized can be glucose saturated ethanol solution.

In step (S42), the solution can be atomized by the atomizer 710 in one embodiment. The size of the micro-scaled droplets can be in a range from about 1 micrometer to about 10 micrometers.

In step (S43), the electric potential is a negative or positive electric potential ranged from about −2000V to about +2000V. In one embodiment, the electric potential is about −1800V or about +1800V.

In step (S44), when the micro-scaled droplets passing through the at least one through-hole, the electrons can transfer between the charged electrode and the micro-scaled droplets. The sign of the micro-scaled droplets depends on the sign of the charged electrode. For example, the charged electrode is negative, the electrons transferred from the charged electrode to the micro-scaled droplets.

Depending on the embodiment, certain of the steps of methods described may be removed, others may be added, and the sequence of steps may be altered. The description and the claims drawn to a method may include some indication in reference to certain steps. However, the indication used is only to be viewed for identification purposes and not as a suggestion as to an order for the steps. 

What is claimed is:
 1. A method for making charged nanoparticles, the method comprising: providing a solution with a first solute, wherein the solution is a saturated solution with a volatile solvent; atomizing the solution into micro-scaled droplets; providing a charged electrode with at least one through-hole, wherein a negative or positive electric potential is applied to the electrode; allowing the micro-scaled droplets to pass through the at least one through-hole.
 2. The method as claimed in claim 1, wherein a solvent of the solution is water or ethanol.
 3. The method as claimed in claim 1, wherein the solution is a NaCl saturated ethanol solution or a glucose saturated ethanol solution.
 4. The method as claimed in claim 1, wherein the solution is atomized by an atomizer.
 5. The method as claimed in claim 1, wherein the solution with the first solute is atomized into micro-scaled droplets with the first solute.
 6. The method as claimed in claim 1, wherein the electric potential is in a range from about −2000V to about +2000V.
 7. The method as claimed in claim 6, wherein the electric potential is about −1800V or about +1800V.
 8. The method as claimed in claim 1, wherein a size of the micro-scaled droplets ranges from about 1 micrometer to about 10 micrometers.
 9. The method as claimed in claim 1, wherein a size of the at least one through-hole is equal to or less than 1 millimeter. 